HWM 128 Automatic Roof Tile Making Machine
HWM-128 Roof tile making machine,specially to make concrete roof tile using the Cement and sand and water as raw material,with the forming style at Pressing,adopts Japanese Mitsubishi PLC,Concrete roof tile machine the working process is automatic controlled,Automatic Roof Tile Making Machine the production speed can up to 6-8pcs per min.
HWM-128 Roof tile making machine is a multifunctional machine,Automatic Concrete Mixer it can produce different types of roofing tile only by changing the mould.We accept custom roof tile mould,roof tile machine it allows the customer logo to be made in the roof tile mould, Roof Tile Making Machine thus to get the finished roof tile with customer logo.
I.Technical data of HWM-128 Roof Tile Making Machine
Press and sieve
Power for roof tile machine only
Power for Concrete mixer
Mainframe size (L×W×H)
Weight of roof tile machine
Weight of concrete mixer
II.Section drawing of HWM-128 Roof tile machine with Concrete mixer
III. Production process description of HWM-128 Roof tile making machine
The raw material will be transferred to Concrete mixer through the skip hoist bucket hopper,after mixing ,Concrete Roof tile making machine the mixed material (cement and fine sand and water) will be discharged to the Rational mixer.
The mixed material will be discharged to the mould through a ration cup ensure the quantity of mateiral is accurate,so the roof tile getting from the machine with same thickness and weight.
Raw materials should be mixed with concrete mixer for 5~10 mins. This production line is equipped with JQ-350 Concrete mixer. ( exceeding capacity 350L, ￠1300mm, 12rpm)
P.O or P.S 32.5#
Should be qualified
1.cement：sand = 1:1.5～2.0(weight)
2. water : cement = 1:0.25～0.35. The water should not be too much, otherwise tile will stick to mould.
3.The quantity of clay or mud contain in raw materials should not be over 3%, otherwise quality will be affected.
4. The weight of roof tile at the size of 424x337mm is about 4.2kg/pc
The roof tile with steel pallet will be put in the curing rack after forming, generally,it requires to keep the curing rack for 24 hours, and the roof tile can be removed from the steel pallet in the second day to keep in the stock yard.
It requires to spraying the water to roof tile three times a day in the first week,the quantity of water subject to humidity. The roof tile are suggested to keep in vertical way.
All the tile are suggested to be painted before selling.Color is painted after tile completely dried ( water moisture content not over 2%). First painting for bottom layer with temperature range 50℃～60℃, after dried then paint the surface layer.
Painting job can be done by manually or by automatic painting production line.
V. Roof Tile Mould Introduction:
Different types of roof tiles made by our customer,mould could be made according to customer’s drawing.
Steel Mould for mail tile:
Upper mould is made of Cr12,down mould made of S45 and mould frame is made of 40# steel. The lifespan is 300 thousands times.
Steel Pallet for roof tile production purpose
5. Roof Tile Accessories:
Normally they are made of plastic. Steel mould also could design if required by buyer.
Steel pallet for roof tile machine production loading into container
VI .HWM-128 Roof tile machine working at site
Flat tile made by HWM-128 Roof tile machine
Roof tile Application：